TABLE OF MECHANICAL PROPERTIES (ASTM) FOR TITANIUM BAR AND BILLET
|
|
|
yield Strength (0.2%offset) min or range |
|
elongation In 4d |
reduction Of area |
|
|
grade |
ksi |
mpa |
ksi |
mpa |
min.% |
min.% |
|
1 |
35 |
240 |
20 |
138 |
24 |
30 |
|
2 |
50 |
345 |
40 |
275 |
20 |
30 |
|
2h |
58 |
400 |
40 |
275 |
20 |
30 |
|
3 |
65 |
450 |
55 |
380 |
18 |
30 |
|
4 |
80 |
550 |
70 |
483 |
15 |
25 |
|
5 |
130 |
895 |
120 |
828 |
10 |
25 |
|
6 |
120 |
828 |
115 |
795 |
10 |
25 |
|
7 |
50 |
345 |
40 |
275 |
20 |
30 |
|
7h |
58 |
400 |
40 |
275 |
20 |
30 |
|
9 |
90 |
620 |
70 |
483 |
15 |
25 |
|
9i |
90 |
620 |
70 |
483 |
12 |
25 |
|
11 |
35 |
240 |
20 |
138 |
24 |
30 |
|
12 |
70 |
483 |
50 |
345 |
18 |
25 |
|
13 |
40 |
275 |
25 |
170 |
24 |
30 |
|
14 |
60 |
410 |
40 |
275 |
20 |
30 |
|
15 |
70 |
483 |
55 |
380 |
18 |
25 |
|
16 |
50 |
345 |
40 |
275 |
20 |
30 |
|
16h |
58 |
400 |
40 |
275 |
20 |
30 |
|
17 |
35 |
240 |
25 |
170 |
24 |
30 |
|
18 |
90 |
620 |
70 |
483 |
15 |
25 |
|
18i |
90 |
620 |
70 |
483 |
12 |
20 |
|
19ii |
115 |
793 |
110 |
759 |
15 |
25 |
|
19iii |
135 |
930 |
130 to 159 |
897 to 1096 |
10 |
20 |
|
19e |
165 |
1138 |
160 to 185 |
1104 to 1276 |
5 |
20 |
|
20ii |
115 |
793 |
110 |
759 |
15 |
25 |
|
20iii |
135 |
930 |
130 to 159 |
897 to 1096 |
10 |
20 |
|
20iv |
165 |
1138 |
160 to 185 |
1104 to1276 |
5 |
20 |
|
21ii |
115 |
793 |
110 |
759 |
15 |
35 |
|
21iii |
140 |
966 |
130 to 159 |
897 to 1096 |
10 |
30 |
|
21iv |
170 |
1172 |
160 to 185 |
1104 to 1276 |
8 |
20 |
|
23 |
120 |
828 |
110 |
759 |
10 |
15 |
|
23i |
120 |
828 |
110 |
759 |
7.5 v,6.0vi |
25 |
|
24 |
130 |
895 |
120 |
828 |
10 |
25 |
|
25 |
130 |
895 |
120 |
828 |
10 |
25 |
|
26 |
50 |
345 |
40 |
275 |
20 |
30 |
|
27 |
35 |
240 |
25 |
170 |
24 |
30 |
|
28 |
90 |
620 |
70 |
483 |
15 |
25 |
|
28i |
90 |
620 |
70 |
483 |
12 |
20 |
|
29 |
120 |
828 |
110 |
759 |
10 |
25 |
|
29i |
120 |
828 |
110 |
759 |
7.5 v,6.0vi |
15 |
|
30 |
50 |
345 |
40 |
275 |
20 |
30 |
|
31 |
65 |
450 |
55 |
380 |
18 |
30 |
|
32 |
100 |
689 |
85 |
586 |
10 |
25 |
|
33 |
50 |
345 |
40 |
275 |
20 |
30 |
|
34 |
65 |
450 |
55 |
380 |
18 |
30 |
|
35 |
130 |
895 |
120 |
828 |
5 |
20 |
|
36 |
65 |
450 |
60 to 95 |
410 to 655 |
10 |
|
|
37 |
50 |
345 |
31 |
215 |
20 |
30 |
|
38 |
130 |
895 |
115 |
794 |
10 |
25 |
|
above Properties apply to longitudinal sections up to 3 inch thickness With maximum of 10 inch. Mechanical properties of larger Sections shall be negotiated between the manufacturer and Purchaser. |
||||||
|
i) Properties for material in transformed-beta condition. |
||||||
|
ii) Properties for solution treated condition. |
||||||
|
iii) Properties for solution treated and aged condition-moderate Strength (determined by aging temperature). |
||||||
|
iv) Properties for solution treated and aged condition-high Strength (determined by aging temperature). |
||||||
|
v) For product section or wall thickness values < 1.0 in. |
||||||
|
vi) For product section or wall thickness values_> 1.0 in. |
||||||