Ti-15-3-3-3 Titanium Plate For Glasses

Implementation standard AMS4914 AMS 4911 ASTM B265 Density: 4.77g/cubic meter Surface treatment: pickling, polishing, passivation, etc. to improve its corrosion resistance and appearance. Thickness: 0.5mm-60mm, thickness can be customized according to different application requirements....

Send Inquiry

Product Introduction

Implementation standard AMS4914 AMS 4911 ASTM B265
Density: 4.77g/cubic meter
Surface treatment: pickling, polishing, passivation, etc. to improve its corrosion resistance and appearance.
Thickness: 0.5mm-60mm, thickness can be customized according to different application requirements.

Production process: cold rolling and hot rolling
Surface treatment: pickling or passivation
Thickness: 0.5mm-60mm, thickness can be customized according to different application requirements.

Ti-15-3-3-3 chemical composition

Brand	Main ingredient%			Impurities/%, not more than
Ti-15333	AL	Cr	V	Fe	C	H	O	Other elements
	2.8~3.6	2.5~3.5						single	sum
			14.0~16.0	0.25	0.05	0.015	0.13	0.10	0.30

Mechanical properties at room temperature (Tensile Test)

Requirement

Tensile Strength

(Mpa)

Yield Strength, 0.2% Offset (Mpa)

Elongation in 2 in. or 50mm (%)

600-945

650-900

≥1

Ti-15-3-3-3 titanium alloy plate

Ti15333 process flow

Ti15333 titanium alloy plate, as a high-performance titanium alloy, not only shows a wide range of application prospects in aerospace, medical equipment and chemical fields.
Starting from the careful selection and pretreatment of raw materials, its production has entered a delicate and complex link. The melting and casting process requires extremely high temperature control and process accuracy to ensure that the alloy composition is uniform and without obvious defects. The subsequent heat treatment process further regulates the microstructure and properties of the material through a series of carefully designed steps such as annealing, solution treatment and aging treatment. Machining and surface treatment are the key steps to finely carve this alloy, aiming to improve its surface finish and corrosion resistance. Finally, after strict quality inspection and performance testing, it can meet the needs of various high-end applications with its excellent performance and reliability.

Performance characteristics of Ti-15-3-3-3 titanium alloy

Mechanical properties: Ti15333 titanium alloy has high strength and excellent fatigue resistance. Through aging treatment, its strength can reach more than 1080MPa. In addition, the elastic modulus of this alloy is low, about 80GPa, which is slightly higher than the elastic modulus of titanium-nickel shape memory alloy (about 60GPa). It has high elastic recovery and is suitable for applications that require large-distance bending without permanent deformation. 12.
Processing performance: Ti15333 titanium alloy has good cold rolling and cold forming properties, and the cold rolling deformation can reach more than 90%. It can form medium-complex sheet metal parts at room temperature. It can also be superplastic formed above 700℃ and is suitable for the production of cold heading rivets and bolts. In addition, the alloy has good welding performance ‌2.
‌Corrosion resistance‌: Ti15333 titanium alloy has excellent environmental corrosion resistance and is suitable for use in various corrosive environments‌.