GR5 Titanium Tube

GR5 titanium tube is a titanium alloy tube, also known as Ti-6Al-4V, which is one of the common and important titanium alloys.

Send Inquiry

Product Introduction

GR5 titanium alloy pipe is a pipe product made of GR5 titanium alloy material. GR5 titanium alloy is a high-temperature, lightweight titanium alloy composed of titanium (Ti) and aluminum (Al) alloy combination, which contains 5% aluminum and 4% pearl. This alloy has excellent mechanical properties and corrosion resistance, so it is widely used in various fields.

Product Name: GR5 Titanium Tube

Grade: Pure Titanium GR5

mark Standard: According to the standards of the American Society for Testing and Materials (ASTM), ASTM B861, ASTM B338, etc.

The manufacturing process is divided into: seamless pipe welded pipe extrusion pipe forging pipe

The manufacturing method is divided into: cold rolling extrusion

Specifications: Diameter: φ 20-φ60mm wall thickness 0.6-3mm ≤8000

φ60--108mm 1.5--5mm ≤6000

Manufacturing process: rolling

main feature

1. Medium-strength titanium alloy products containing 6% aluminum and 4 % vanadium .

2.welded constructions with operating temperatures up to 600 ° F.

3. Light weight , high strength, good formability and strong corrosion resistance.

GR5 Titanium TubeChemical composition list

Grade	Nominal chemical composition		Chemical composition (mass fraction%)
			main ingredient
		Ti	AI	V	h
GR5	Ti-6AL-4V	%	%	%	Maximum %
GR5	Ti-6AL-4V	88.74-91.0	5.5-6.75	3.5-4.5	0.015

Greenhouse Mechanical Properties of Sheets

Greenhouse Mechanical Properties of Sheets
Grade	state	Thickness/mm	Tensile strength R/Mpa	Specified non-proportional extension strength R _0.2/Mpa	Elongation after breaking A/%
Gr1ELI	m	0.3～25.0	≥200	≥140	≥30
Gr1	m	0.3～25.0	≥240	≥170	≥25
Gr2	m	0.3～25.0	≥４００	≥２７５	≥２５
Gr3	m	０.３～２５.０	≥５００	≥３８０	≥２０
Gr4	m	０.３～２５.０	≥５８０	≥４８５	≥２０
Gr5	m	０.８～４.７５	≥９２５	≥８７０	≥１０
Gr5	m	＞4.75～２５.０	≥８９５	≥８３０	≥１０
Gr23	m	0.8～25.0	≥860	≥795	≥10
a For pure titanium with a thickness less than 0.64mm and for plates with a thickness not greater than 1.60mm, the elongation after fracture shall be reported as the measured

GR5Titanium tube inspection standards and methods

project	Detection method
Flattening experiment	When requested by the buyer and indicated in the contract, the flattening test shall be carried out
Water (air) pressure test	When requested by the purchaser and specified in the contract, the pipes shall be subjected to hydraulic or air pressure tests, and the test method selected by the purchaser shall be specified in the contract. If it is not specified in the contract, the supplier may not carry out the experiment, but must ensure that it complies with
bending experiment	When required by the buyer and specified in the contract, the pipe with an outer diameter of no more than 60mm shall be subjected to a bending test, the diameter of the bending core shall be 12 times the outer diameter of the pipe, and there shall be no cracks on the surface of the pipe after cold bending at 90°. The TA3 pipe bending test index is determined by the supplier and the buyer through negotiation
Dimensions and Tolerances	should comply with the standard
Appearance Quality	The inside and outside of the tube should be clean, free of visible defects such as cracks, folds, peeling, pinholes, etc.
Chemical composition analysis method	According to GB/T4689
Mechanical property test method	According to GB/T228
Process performance test method	The flattening test is carried out according to GB/T246, the water pressure test is carried out according to GB/T241, the air pressure test is carried out according to the method approved by both parties, and the bending test is carried out according to GB/T244
Dimensional measurement inspection method	Corresponding precision gauge measurement
Appearance quality inspection method	Visual inspection
Note: GB/T3625-2010, ASTM B338 standard titanium tubes are compared with GB/T3624-2010, ASTM B337 standard titanium alloy tubes multi-flare test and ultrasonic flaw detection two inspection items, ultrasonic flaw detection should comply with GB/T12969 regulations

GR5Titanium TubeApplication fields:

Avionics business: widely used in the aviation field, including aircraft underlying components, motor components, connectors, screws and buckles, etc. Its high strength, light weight, corrosion resistance and other characteristics make it the best material for assembling light aviation parts.

Clinical devices: Because of its good biocompatibility and consumption resistance, it is widely used in the field of clinical devices. For example, clinical devices such as prosthetic joints, dental inserts, bone plates and screws are mostly produced using GR5 titanium tubes to meet biocompatibility and mechanical strength requirements.

Synthetic industry: It has significant consumption protection against acids, antacids, saline water and oxidizing media and is therefore widely used in the synthetic industry. Used to produce composite materials, petrochemical pipelines, refinery spiers, storage tanks, etc., and can withstand harsh damaging conditions.

Automotive Industry: It is used in the automotive industry to produce parts such as exhaust systems, turbochargers, and suspension systems. Its high strength and lightweight properties help further develop the vehicle's performance and environmental friendliness.

Outdoor products: Because of its high strength and low consumption, it is mostly used to make high-end outdoor products, such as golf clubs, bicycle profiles, tennis rackets, cast poles, etc.

Other fields: widely used in marine engineering, electronic equipment, cosmetic containers, spectacle frames, jewelry and other fields.