6al4v Metal Titanium Wire

Pure titanium is a silver-white metal with many excellent properties.
The density of titanium is 4.54g/cm3, which is 43% lighter than steel and slightly heavier than the famous light metal magnesium.
The mechanical strength is about the same as steel,
twice as strong as aluminum, and five times stronger than magnesium.
Titanium is resistant to high temperatures, with a melting point of 1942K,
which is nearly 1000K higher than gold and nearly 500K higher than steel.

Send Inquiry

Product Introduction

6Al-4V titanium alloy, usually abbreviated as 6-4 titanium alloy, is a common α-β titanium alloy, which contains 6% aluminum (Al) and 4% vanadium (V), and the remaining main components are Titanium (Ti) with extremely high rare earth content. The alloy offers a range of excellent performance characteristics, including high strength, excellent corrosion resistance, thermal strength and biocompatibility .

Product name: 6ai4v titanium wire

Brand: GR5 BT6

Implementation standards: ASTMF136 ASTM B348

ASTM F67

Density: 4.51g/cm3

chemical composition list
Fe (highest)	C (highest)	N (highest)	H (highest)	O (highest)	Al (highest)	v (highest)	Ti (highest)	element	element
								most (each)	total
0.4	0.08	0.05	0.012	0.13	5.50~6.5	3.5~4.5	balance	0.1	0.4

MECHANICAL PROPERTIES
Yield Strength(0.2%Offset		UItimate Tensile Strength		Elongation0.2% Offset	Reduction Of Aera
Min		Min		Min %	%
Ksi	MPa	Ksi	MPa
120	828	130	895	10	25

Heat treatment of finished Alloy Wire products
Alloy Wire delivery status	type	temperature		Time(Hr)	cool down
		°C	°F
annealing	stress relief	480	900	0.5 – 2	Air
elastic tempering	stress relief	250	480	0.5	Air

Room temperature properties of wire
Trademark	state	Diameter/mm	Greenhouse mechanical properties
Trademark	state	Diameter/mm	R/MPa	A/%
TA1ELI	M	3.2~7.0	≥200	≥30
TA1	M		≥240	≥24
TA2	M		≥400	≥20
TA3	M		≥500	≥18
TA4	M		≥580	≥15
TA1ELI	M	0.5~＜3.2	≥200	≥18
TA1	M		≥240	≥15
TA2	M		≥400	≥12
TA3	M		≥500	≥10
TA4	M		≥580	≥8
TC4	M	1.0~2.0	≥925	≥8
TC4	M	≥2.0~7.0	≥895	≥10

Important features

Excellent strength to weight ratio

Higher strength at ambient temperature than grades 1 and 2

Good creep resistance at temperatures up to approximately 300 °C (570 °F)

Outstanding corrosion resistance in most natural environments and many industrial process environments

Density is about half that of nickel alloys

application

Ti-6al-4v is a titanium alloy strengthened by heat treatment. It has good weldability, sheet formability and forging performance. Used to manufacture jet engine compressor blades, impellers, etc. Others such as landing gear wheels and structural parts, fasteners, brackets, aircraft accessories, frames, stringer structures, and pipes are widely used .